大容量中频变压器铁心材料损耗特性及其应用可行性

电工钢 ›› 2025, Vol. 7 ›› Issue (2): 38-.

大容量中频变压器铁心材料损耗特性及其应用可行性

马光¹, 钱肖², 何承绪¹, 徐伟杰³, 韩钰¹, 黎先浩⁴, 方晨²

（1.先进输电技术全国重点实验室，中国电力科学研究院有限公司，北京 100192；
2.国网浙江省电力有限公司金华供电公司，浙江金华 321000；
3.国网（西安）环保技术中心有限公司，陕西西安 710100；
4.首钢智新电磁材料（迁安）股份有限公司，河北迁安 064404）

出版日期:2025-04-28 发布日期:2025-05-06

Research on the magnetic properties and application feasibility of iron core materials for large capacity medium frequency transformers

MA Guang¹, QIAN Xiao², HE Chengxu¹, XU Weijie³, HAN Yu¹, LI Xianhao⁴, FANG Chen²

(1. State Key Laboratory of Advanced Power Transmission Technology, China Electric
Power Research Institute, Beijing 100192, China; 2. Jinhua Power Supply Company,
State Grid Zhejiang Electrical Power Co.,Ltd., Jinhua 321000, China; 3. State Grid
(Xian) Environmental Protection Technique Center Co.,Ltd., Xian 710100, China;
4. Shougang Zhixin Electromagnetic Material (Qianan) Co.,Ltd., Qianan 064404, China)

Online:2025-04-28 Published:2025-05-06

摘要/Abstract

摘要： 分析了两种硅钢材料在中频工况下的损耗特性，研究了频率、温度对损耗特性的影响规律，同时探索了两种硅钢材料在大容量中频变压器的应用可行性。结果表明，频率提升，两种带材损耗均大幅提升。在频率＜400 Hz条件下，0.15 mm薄规格取向硅钢损耗相对较低；在频率＞400 Hz条件下，0.08 mm超薄取向硅钢损耗相对较低。两种硅钢材料在60~130 ℃复杂工况条件下损耗均呈降低趋势，温度越高、加热时间越长，损耗逐渐降低，最终达到平稳状态。仅从材料性能角度考虑，当频率≤400 Hz时，大容量中频变压器铁心材料选用0.15 mm薄规格取向硅钢较为合适，当频率＞400 Hz时，大容量中频变压器铁心材料选用0.08 mm薄规格取向硅钢较为合适。

关键词: 薄规格取向硅钢, 超薄取向硅钢, 损耗, 复杂工况, 中频变压器

Abstract: The loss characteristics under medium frequency work conditions of two silicon steel materials were analyzed, the effect of frequency, temperature on loss property was studied, and application feasibility of two silicon steel materials in large capacity medium frequency transformers. 0.15 mm thin-gauge oriented silicon steel has lower loss below 400 Hz, while 0.08 mm ultra-thin grain-oriented silicon steel has lower loss above 400 Hz.The iron loss of both silicon steel materials under 60-130 ℃ complex conditions were decreased. The higher the temperature and the longer the heating time, the loss gradually decreases and finally reaches a stable state. Just from performance perspective, when the frequency ≤400 Hz, 0.15 mm thin-gauge grain-oriented silicon steel was more suitable for preparing large capacity medium frequency transformer cores, when the frequency ＞400 Hz, 0.08 mm ultra-thin grain-oriented silicon steel was more suitable for preparing large capacity medium frequency transformer cores.

Key words: thin-gauge grain-oriented silicon steel, ultra thin grain-oriented silicon steel, Iron loss, complex working conditions, medium frequency power transformers

马光, 钱肖, 何承绪, 徐伟杰, 韩钰, 黎先浩, 方晨. 大容量中频变压器铁心材料损耗特性及其应用可行性[J]. 电工钢, 2025, 7(2): 38-.

MA Guang, QIAN Xiao, HE Chengxu, XU Weijie, HAN Yu, LI Xianhao, FANG Chen. Research on the magnetic properties and application feasibility of iron core materials for large capacity medium frequency transformers[J]. Electrical Steel, 2025, 7(2): 38-.

[1]	文倩, 李洋, 姜伟宁, 武晓龙, 杨平, 张海利. 等温退火温度对薄规格取向硅钢二次再结晶行为的影响[J]. 电工钢, 2023, 5(6): 1-7.
[2]	王晓燕, 李国保, 曹剑飞, 宋刚. 立体卷铁心的单框损耗测量试验及验证[J]. 电工钢, 2023, 5(4): 32-.
[3]	胡明睿, 朱英杰, 赵益鋆, 王放秋, 沈校, 方烽. 新能源汽车驱动电机用无取向硅钢性能分析[J]. 电工钢, 2023, 5(3): 28-33.
[4]	张凤泉, 汪水泽. 电力变压器发展及能效升级对取向硅钢需求的影响[J]. 电工钢, 2022, 4(5): 6-.
[5]	张凤泉, 汪水泽. 中小电机新能效等级对无取向电工钢需求的影响[J]. 电工钢, 2022, 4(4): 21-.
[6]	杨平, 李洋, 顾新福, 张海利, 贾志伟. 薄规格取向硅钢晶粒异常长大时的组织、织构稳定性与表面效应分析[J]. 电工钢, 2021, 3(5): 1-.
[7]	张海利, 贾志伟, 李洋, 罗理, 张静, 李莉, 杨平, 蒋奇武. 0.20 mm薄规格取向硅钢的开发及关键工艺探讨[J]. 电工钢, 2021, 3(5): 10-.
[8]	王晓燕, 孙亮, 陶利, 梁庆宁, 宋刚. 取向硅钢在立体卷铁心中的服役特性研究[J]. 电工钢, 2021, 3(1): 1-.
[9]	裴英豪, 刘青松, 施立发, 夏雪兰, 祁旋. 氧化性气氛对Fe-2 ％Si无取向电工钢电磁性能的影响[J]. 电工钢, 2020, 2(5-6): 14-.
[10]	张俊鹏, 张晗, 向前, 黄双, 康勃. 爱泼斯坦方圈法测定硅钢片比总损耗不确定度评定[J]. 电工钢, 2020, 2(4): 39-.
[11]	程灵, 马光, 胡卓超, 龚卫国, 杨富尧, 孟利, 董瀚, 陈新. 0.18 mm极低损耗取向硅钢电磁特性与铁心性能仿真分析#br#[J]. 电工钢, 2020, 2(1): 15-21.
[12]	骆新根, 黄咸波, 郭小龙, 杨佳欣, 申明辉. 冷轧压下率对薄规格取向硅钢冷轧和退火织构的影响[J]. 电工钢, 2019, 1(2): 21-28.