Experimental research on silicon steel 100AW800DC for iron core material of high performance electromagnetic switch

JIANG Fujian 1,GAO Zhenyu 1,LI Yuanhua2,ZHANG Renbo1,LIU Wenpeng1,LI Hao2，CHEN Dongmei3,LIU Haitao3

1.Iron and Steel Research Institute of Ansteel Group Corporation,Anshan 114009,China;
2.Cold Rolling Silicon Steel Plant of Anshan Iron & Steel Co. Ltd.,Anshan 114021,China;3.State Key Laboratory of Rolling & Automation, Northeastern University, Shengyang 110819, China

Online:2020-10-28 Published:2020-10-30

摘要/Abstract

摘要： 通过工业生产结合实验室退火试验研究，成功研制出高性能的电磁开关铁心材料100AW800DC，其性能达到电磁开关铁心材料的
先进水平，横向厚度偏差约为26 μm，在平均晶粒尺寸约60～80 μm范围内，所获得的电磁性能最佳。通过模拟产线退火试验，在870 ℃加热4 min44 s条件下，可以获得铁损P1.5/50达到最低5.826 3 W/kg、磁感应强度B2500为1.631 8T、硬度HV5为159、屈服强度Rp0.2为324 MPa的材料性能。

关键词: 电磁开关, 铁心材料, 磁感应强度, 铁损

Abstract: A silicon steel 100AW800DC, which is one of the iron core material of high performance electromagnetic switch, has been successfully developed by combining industrial production with laboratory annealing experiment. Its performance has reached the advanced level of electromagnetic switch iron core material. And the electromagnetic properties will be the best when the transverse thickness deviation is about 26 μm and the range of average grain size from 60 μm to 80 μm. Through simulated annealing experiment of production line, the properties of 100AW800DC with the lowest core loss P1.5/50 of 5.826 3 W/kg, magnetic induction intensity B2500 of 1.631 8 T, hardness HV5 of 159 and yield strength Rp0.2 of 324 MPa can be obtained in the condition of heating time 4 min44 s at 870 ℃.

Key words: electromagnetic switch, iron core material, magnetic induction intensity, iron loss

姜福健, 高振宇, 李元华, 张仁波, 刘文鹏, 李浩, 陈冬梅, 刘海涛. 高性能电磁开关铁心材料100AW800DC的试验研究[J]. 电工钢, 2020, 2(4): 17-.

JIANG Fujian , GAO Zhenyu , LI Yuanhua, ZHANG Renbo, LIU Wenpeng, LI Hao, CHEN Dongmei, LIU Haitao. Experimental research on silicon steel 100AW800DC for iron core material of high performance electromagnetic switch[J]. Electrical Steel, 2020, 2(4): 17-.

[1]	杨平, 武晓龙, 顾新福, 裴伟, 冷烨旻. 电工钢在线铁损数据分析及钢卷评价系统建立[J]. 电工钢, 2020, 2(4): 6-.
[2]	(译)王杰, 潘妮. 取向电磁钢板一次被膜附着性改进措施[J]. 电工钢, 2020, 2(4): 49-.
[3]	(译)王杰, 潘妮. 铁损和磁致伸缩性能均优良的取向电磁钢板磁畴细化方法#br#[J]. 电工钢, 2020, 2(4): 54-.
[4]	(译)王杰, 潘妮. 用激光刻痕实现耐热磁畴细化[J]. 电工钢, 2020, 2(4): 59-.
[5]	李秀章, 周新华. 取向电工钢片铁损分布不均匀性测量分析[J]. 电工钢, 2019, 1(1): 16-18.
[6]	朱业超, 田文洲, 骆忠汉, 胡守天, 孙亮, 郭小龙, 程祥威. 磁畴结构对取向硅钢磁致伸缩的影响[J]. 电工钢, 2019, 1(1): 19-22.