Changes of inclusions composition in the EH36 ship plate steel during production process

Online:2021-04-05 Published:2021-03-30

摘要/Abstract

摘要： 对采用“BOF→LF→RH→CC”工艺生产EH36船板钢过程中的夹杂物进行了研究。用SEM-EDS分析了试样中的夹杂物形貌和成分，用FactSage软件计算了夹杂物的析出情况。研究表明：LF进站钢液中夹杂物主要为SiO₂，试样中的MnS是在试样凝固过程中形成的。Ca处理后，液态夹杂物数量增多。经过RH处理后，夹杂物中Al₂O₃含量升高，CaO和MgO含量降低。中间包钢液中夹杂物的Al₂O₃含量降低，CaO含量升高，夹杂物与渣发生反应，使夹杂物成分向低熔点区靠近。中间包渣中SiO₂含量较高，与钢中Al发生反应，使钢液中Si含量升高，Al含量降低。钢液凝固过程中发生成分偏析，使铸坯中夹杂物的S含量明显升高，Al₂O₃含量升高，CaO含量降低。在铸坯中形成了CaO和Al₂O₃比例不同的钙铝酸盐夹杂物以及Al₂O₃夹杂物，且部分钙铝酸盐表面形成CaS。

关键词: 船板钢, 夹杂物, 连铸坯, 炉渣, 硫化物

Abstract: The inclusions of EH36 ship plate steel produced by “BOF→LF→RH→CC” process were studied. The morphology and composition of inclusions in the sample were analyzed by SEM-EDS，and the precipitation of inclusions were calculated by Factsage software. The research showed that inclusions were mainly SiO₂ when the molten steel was hoisted into LF furnace，and MnS of the sample was formed during solidification of the sample. The number of liquid inclusions was increased after calcium treatment. Al₂O₃ content of inclusions was increased and the content of CaO and MgO were decreased after RH refining. Al₂O₃ content of inclusions was decreased and CaO content of inclusions was increased in tundish. The composition of inclusions was close to the low melting point zone due to the inclusions reacting with slag. SiO₂ content of slag was high and it reacted with Al of molten steel，which caused to increase Si content and reduce Al content in the molten steel. Because composition segregation occurred during solidification of molten steel，S content of inclusions was significantly increased，Al₂O₃ content of inclusions was increased and CaO content of inclusions was decreased. Calcium aluminate inclusions with different ratios of CaO and Al₂O₃ and Al₂O₃ inclusions were formed in the billet，and CaS was formed on the surface of some calcium aluminate.

Key words: ship building steel, inclusion, continuous casting slab, slag, sulfide

黄治成, 田俊, 叶锦涛, 阿迪力·艾力. EH36船板钢生产过程中夹杂物成分的变化[J]. 炼钢, 2021, 37(2): 62-69.

[1]	张旭彬, 张立峰. 低碳钢和超低碳钢连铸板坯皮下凝固钩的特征与控制研究[J]. 炼钢, 2021, 37(2): 1-9.
[2]	许苗苗, 尚正鸿, 凌海涛, 常立忠. 316L不锈钢精炼过程中夹杂物成分演变[J]. 炼钢, 2021, 37(2): 16-22.
[3]	朱万军, 周甫, 王春锋, 沈继胜, 邱晨. CSP流程薄规格高强钢夹杂物控制研究[J]. 炼钢, 2021, 37(2): 51-57.
[4]	魏国立, 朱青德, 胡绍岩, 朱荣, 冯超. 120 t转炉底吹CO₂工艺研究及应用[J]. 炼钢, 2021, 37(1): 8-13.
[5]	姜敏, 李凯轮, 王昆鹏, 徐建飞, 王郢, 万文华, 王新华. 低氧高碳铬轴承钢LF-VD精炼时洁净度与夹杂物特征变化[J]. 炼钢, 2021, 37(1): 27-32.
[6]	李婷婷, 杨健, 黄福祥, 朱克然, 裴兴伟. 连铸坯凝固钩形成机理与控制技术综述[J]. 炼钢, 2021, 37(1): 44-56.
[7]	李成斌, 刘君, 蒋鹏. 车轴钢EA1N全流程夹杂物演变分析及工艺优化[J]. 炼钢, 2021, 37(1): 73-80.
[8]	黄日康, 张立峰, 姜仁波, 郭银涛, 杨文, 段豪剑, 姜东滨, 张献光. 超低碳铝脱氧钢连铸过程钢中非金属夹杂物的演变[J]. 炼钢, 2020, 36(6): 39-45.
[9]	王瑞刚, 姜敏, 王新华. 超低碳电池壳砂眼缺陷冶金诱因与钢液洁净度的影响研究[J]. 炼钢, 2020, 36(6): 49-53.
[10]	温瀚. SCX400车轮钢非金属夹杂物控制工艺研究与实践[J]. 炼钢, 2020, 36(6): 54-60.
[11]	付振坡, 赵晓萍, 李双江, 李泉稷, 罗应明. 风电钢焊后热影响区探伤不合原因分析[J]. 炼钢, 2020, 36(6): 67-71.
[12]	田博, 孙立根, 朱立光. 高温条件下Mg处理船体钢钉扎粒子的作用行为[J]. 炼钢, 2020, 36(6): 72-77.
[13]	王德永, 屈天鹏. 镁洁净钢新技术发展与展望 [J]. 炼钢, 2020, 36(5): 1-13.
[14]	卢金霖, 张东升, 罗志国, 邹宗树. 旋流中间包夹杂物聚合行为的数值模拟[J]. 炼钢, 2020, 36(5): 37-43.
[15]	程淑勇, 赵显久, 王波, 张捷宇. 含Ti超低碳钢浸入式水口结瘤研究[J]. 炼钢, 2020, 36(5): 58-62.