Abstract:

The oxide skin structures of high grade non-oriented silicon steel and carbon steel produced by hot rolling were comparative analyzed. A series of pickling experiments were carried out on a normalizing and pickling production line of silicon steel. The influences of pickling temperature, acid concentration and shot blasting on pickling time and effect were investigated. It is considered that the difficulty in pickling the oxide sheet on the surface of high grade non-oriented silicon steel was due to its special structure. The parameters of pickling process suitable for industrial production of high grade non-oriented silicon steel were given.

Key words:

Non-oriented , silicon , steel,  , pickling , process,  , pickling , line,  , oxide , skin ,