钢包渣线镁碳砖的侵蚀机理分析

摘要/Abstract

摘要： 对某钢厂LF精炼钢包渣线服役前后的镁碳砖进行理化分析、扫描电镜（SEM）-能谱分析（EDS）、Factsage热力学计算、润湿性分析等，研究了镁碳砖的侵蚀机理。研究表明，镁碳砖在钢包内不同的服役温度区域及其自身内部的不同组织结构造成其损毁及侵蚀机理的不同。在近钢液面的高温区域，镁碳砖自身会发生MgO与碳的反应，形成脱碳层。高温下熔渣与镁碳砖的润湿性更好且MgO向熔渣溶解的趋势更大，相比近空气侧的低温区域，镁碳砖受熔渣侵蚀更严重。镁碳砖中，不同MgO骨料颗粒其内部杂质相及组织结构有一定区别。熔渣与镁碳砖中的MgO组元间的润湿性较好，熔渣易对杂质相多、MgO晶粒尺寸较小的骨料进行侵蚀，且易沿MgO晶界渗入MgO骨料内部，造成MgO骨料颗粒的解离并进一步发生反应生成Mg2SiO4。熔渣与镁碳砖之间的氧化还原反应也是其损毁的成因之一。

关键词: 镁碳砖, 侵蚀, MgO溶解度, 润湿性

Abstract: Physical and chemical analysis，SEM-EDS detection，Factsage calculation，wettability analysis of the MgO-C refractory bricks at the slag line of ladle in LF refining before and after service were analyzed，and the erosion mechanism of MgO-C refractory brick was studied. The results showed that，the different temperature of the area where the MgO-C brick locates and the different structure of the MgO-C brick led to the different wear mechanism of refractory. In the hotter area closing to the molten steel，the MgO could react with C and formed a decarburization layer. The wettability between molten slag and MgO-C refractory brick was much better，and the solubility of MgO in the molten slag was much greater. Compared with the cooler area closing to the air，the erosion of MgO-C refractory brick was much serious in the hotter area. There were some differences of the impurity composition and structure between each MgO aggregate. The MgO aggregate with more impurity and small scale of MgO grain would be eroded more easily by molten slag for the good wettability between molten slag and MgO component. The molten slag would penetrate into the MgO aggregate through the grain boundaries，causing the disaggregation of MgO aggregate and the generation of Mg2SiO4 by further reaction. Besides，the redox reaction between molten slag and MgO-C refractory brick was also the main cause of the wear of refractory.

Key words: MgO-C brick, erosion, solubility of MgO；wettability

沈平，张立峰，王祎，杨文. 钢包渣线镁碳砖的侵蚀机理分析[J]. 炼钢.

[1]	贾成橙，唐萍，米晓希，文光华，刘强，侯自兵. 高温激光共聚焦显微镜在熔渣与钢润湿性能研究中的应用[J]. 炼钢, 2017, 33(3): 38-43.
[2]	杨进玲，周立新，潘明旭，余亚平，郭畅，张洲，吕文俊. P91耐热钢探伤分层缺陷成因及改进[J]. 炼钢, 2017, 33(2): 69-.
[3]	陈郑1，廖明1，文敏1，高祝兵2，陈露涛2. RH浸渍管镁铬砖侵蚀分析[J]. 炼钢, 2015, 31(2): 59-61.
[4]	于淑娟1，张大奎1，侯洪宇1,于素荣2，张钟铮3，张新义3. 尘泥团块对鱼雷罐罐衬侵蚀的影响[J]. 炼钢, 2014, 30(5): 62-.
[5]	邓志豪;董元篪;李小虎;王珏;吴六顺. 转炉钢渣对镁质耐火材料的侵蚀过程[J]. , 2013, 29(6): 60-65.
[6]	蔡伟;杨利彬;王东;于文涛;郑丛杰;佟溥翘. 转炉冶炼低碳钢炉衬侵蚀及溅渣冷态模拟和应用[J]. , 2012, 28(4): 7-9,12.
[7]	汪庆国;李京社;唐海燕;王宏斌;宁晓钧. LD→LF→CC工艺生产82B钢的洁净度研究[J]. , 2011, 27(6): 57-61.
[8]	姚亚双;田先明;郑吉红;刘毅;洪学勤. 转炉镁碳质喷补料的研制与应用[J]. , 2011, 27(3): 71-73.
[9]	陈松林;孙加林;熊小勇;王健东;潘波;薛文东;李勇. RH炉用MgO-ZrO2材料抗渣侵蚀机理研究[J]. , 2008, 24(06): 53-56.
[10]	郑宏光;祝方义;刘涛;蔡磁;师金红;陈伟庆. AOD终渣对镁钙质炉衬侵蚀的实验研究[J]. , 2008, 24(02): 26-29.

钢包渣线镁碳砖的侵蚀机理分析

Erosion analysis of MgO-C refractory brick at the slag line of ladle

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 10

编辑推荐

Metrics

本文评价