LF精炼时间对帘线钢夹杂物成分影响

摘要/Abstract

摘要： 针对国内某钢厂生产帘线钢LF精炼时间过长的缺点，在LF精炼过程进行密集取样，系统分析了钢中氧氮含量变化、夹杂物成分演变、数密度、面积百分比以及尺寸变化等，确定了合适的LF精炼时间。研究指出：氧化物夹杂集中分布于轧材中心和边缘部位，部分夹杂物实现了塑性化控制；LF精炼过程，钢中w(T.O)逐渐降
低稳定在20×10^-6，由于扒渣操作，钢液发生二次氧化，精炼开始阶段钢中w(N)迅速增大，逐渐稳定在22×10^-6；当钢中w(Ca)＞1.1×10^-6时，夹杂物中CaO逐渐生成，其类型由SiO2-MnO向CaO-SiO₂-Al₂O₃转变；夹杂物中Al₂O₃主要来源于合金及脱氧剂等辅料，MgO来源于钢包内衬耐材；基于MgO-CaO-SiO₂-Al₂O₃-(MnO)系夹杂物平均成分演变、尺寸所占比例变化以及夹杂物面积百分比变化等，建议将LF精炼过程软吹时间缩短20 min，即整个精炼时间控制在96 min最佳。

关键词: 帘线钢, 夹杂物, 洁净度, 精炼时间

Abstract: In the current study, the effect of LF refining time on the composition of inclusions in tire cord steel was investigated to optimize the LF refining time of a domestic steel plant. Steel samples were taken during LF refining. The evolution of total oxygen and nitrogen contents, and the composition, number density, area fraction, and size of inclusions in steel samples were systematically analyzed to determine an appropriate refining time. It was found that the oxide inclusions were concentrated in the center and edge of the cross section of rolled products and the composition of part of inclusions were controlled in the region of low melting temperature. The total oxygen mass fraction gradually decreased during LF refining and then reached stable to 20×10^-6. Due to the operation of slagging-off after tapping of BOF, the molten steel was oxidized by air, resulting in the rapid increase of nitrogen content at the initial stage of LF refining. The nitrogen mass fraction was then reached a stable value of 22×10^-6during the refining process. When the calcium mass fraction in the molten steel was larger than 1.1×10^-6, the CaO in inclusions was gradually generated and the type of inclusions were transformed from SiO2-MnO to CaO-SiO₂-Al₂O₃. The Al₂O₃ in inclusions mainly came from raw materials such as alloy and deoxidizer. Besides, the MgO in inclusions came from ladle lining. Based on the variation of average composition, size fraction and area fraction of MgO-CaO-SiO₂-Al₂O₃-(MnO) inclusions, the soft blowing time during the current LF refining was suggested to shorten 20 min and the appropriate refining time was proposed as 96 min.

Key words: tire cord steel, inclusion, steel cleanliness, refining time

凌海涛1，郭长波1,2，张立峰1，刘澄2，王广顺2，高永彬2. LF精炼时间对帘线钢夹杂物成分影响[J]. 炼钢, 2016, 32(4): 33-38.

[1]	王举金1，孔祥玉2，孟润泽2，张旭辉2，任英1. Q195热轧带钢脱氧过程非金属夹杂物生成热力学及工业实践[J]. 炼钢, 2020, 36(3): 13-20.
[2]	张建元1，季莎2，张立峰3，陆晓雷1，陈威2，张海礼1. 20CrMnTiH齿轮钢脱氧过程中非金属夹杂物生成热力学及工业实践[J]. 炼钢, 2020, 36(3): 21-26.
[3]	万文1，马德刚2，李经哲2，马旭朝3. 冷轧薄板超低碳钢精炼双联工艺研究及应用[J]. 炼钢, 2020, 36(3): 27-31.
[4]	张国锋1，季莎2，张立峰3，王亚栋2，李彩云1，张威1，罗艳2. 20CrMnTiH齿轮钢凝固和冷却过程中非金属夹杂物的转变研究[J]. 炼钢, 2020, 36(3): 32-38.
[5]	夏兆东1，邓丽琴1，王德永2. 梅钢250t钢包浇铸过程旋涡卷渣行为研究[J]. 炼钢, 2020, 36(3): 44-50.
[6]	安会龙1，任英2*，刘洋2，储焰平2，张彦辉2. 弹簧钢中夹杂物生成热力学[J]. 炼钢, 2020, 36(3): 55-61.
[7]	齐广，王福明，沈伟. 低飞溅气保焊丝钢ER70S-6夹杂物的塑性化控制[J]. 炼钢, 2020, 36(3): 62-67.
[8]	赵晓磊1，成功2，杨华峰1，刘丽娟1，任英2. GCr15轴承钢脱氧过程中非金属夹杂物生成热力学及工业实践 [J]. 炼钢, 2020, 36(2): 22-28.
[9]	王祎,张立峰2，杨文1，雷勋惠1，张继1，赵根安1. Q345钢液凝固及铸坯冷却过程中非金属夹杂物的组成演变[J]. 炼钢, 2020, 36(2): 29-33.
[10]	徐佳林1,2,3，陆海飞1,2,3，田伟光1,2,3，蒋发立2,3. 304不锈钢冷轧板线鳞缺陷改进实践[J]. 炼钢, 2020, 36(2): 70-75.
[11]	屈志东，谢有，孟晓玲，徐建飞，王昆鹏. 高品质轴承钢BOF-LF-RH-CC和EAF-LF-VD-CC工艺夹杂物演变规律[J]. 炼钢, 2020, 36(2): 76-80.
[12]	富强，郭晓春，俞潮. 120 t复吹转炉底吹供气强度和炉底渣层控制的研究[J]. 炼钢, 2020, 36(1): 4-7.
[13]	王建忠1,程礼梅2,任英2,赵晓锋1,李慧峰1,王举金2. 含硫齿轮钢脱氧过程中非金属夹杂物生成热力学及工业实践 [J]. 炼钢, 2020, 36(1): 8-14.
[14]	张明海1，程礼梅2，杨文2，李学科1，于春强1，牛凯军2. 含硫齿轮钢凝固冷却过程中非金属夹杂物的转变研究 [J]. 炼钢, 2020, 36(1): 21-26.
[15]	薛永栋1,2，张威风2，辛雪倩2，李春辉2，杨金安2. 50Cr5MoV支承辊用钢氧和夹杂物控制实践[J]. 炼钢, 2020, 36(1): 67-72.

LF精炼时间对帘线钢夹杂物成分影响

Effect of the LF refining time on the composition of inclusions in tire cord steels

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价